1.4113 X6CrMo17-1 AISI 434 Cold Rolled Stainless Steel Sheet Annealed EN 10088-2
Stainless steels are high-alloy steels. They have high corrosion resistance due to high chromium content of about 4-30%. They are classified in to three types such as ferritic, austenitic, and martensitic steels based on their crystalline structure.
Grade 434 stainless steel contains added molybdenum to increase its corrosion resistance. It is has performance and chemistry similar to that of 430 stainless steel.
The following table shows the chemical composition of grade 434 stainless steel.
| Element | Content (%) |
|---|---|
| Iron, Fe | 81 |
| Chromium, Cr | 16 |
| Molybdenum, Mo | 1 |
| Silicon, Si | 1 |
| Manganese, Mn | 1 |
| Carbon, C | 0.12 |
| Phosphorous, P | 0.040 |
| Sulfur, S | 0.030 |
The physical properties of grade 434 stainless steel are given in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 7.80 cm³ | 0.282 lb/in³ |
| Melting point | 1510°C | 2750°F |
The following table outlines the mechanical properties of annealed grade 434 stainless steel.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 538 MPa | 78000 psi |
| Yield strength (@ strain 0.200%) | 441 MPa | 64000 psi |
| Elastic modulus | 200 GPa | 29008 ksi |
| Poisson's ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 32% | 32% |
| Hardness, Rockwell B (converted from Brinell hardness) | 89 | 89 |
The thermal properties of grade 434 stainless steel are displayed in the following table
201 202 301 304 304l 316 316l 310 410 430 Stainless Steel Sheet/Plate
| Standard: | ASTM A240,ASME SA240,AMS 5524/5507 |
| Thickness: | 0.3 ~ 12.0mm |
| Width Range: | 4'*8ft',4'*10ft',1000*2000mm,1500x3000mm etc |
| Brand name: | TISCO, ZPSS, BAOSTEEL, JISCO |
| Technique: | Cold Rolled ,Hot rolled |
| Forms : | Foils, Shim Sheet, Rolls, Perforated Sheet, Chequered Plate. |
| Applications | Pulp and Paper Textiles Water Treatment |