Hastelloy is a nickel-based corrosion-resistant alloy, which is mainly divided into two categories: nickel-chromium alloy and nickel-chromium-molybdenum alloy. Hastelloy has good corrosion resistance and thermal stability, and is mostly used in aviation, chemical fields, etc.
| Type | Chemical composition of code | Chemical composition.% | ||||||||
| C | Mn | Fe | Si | Cu | Ni | Cr | Mo | W | ||
| SNi6276 | NiCr15Mo16Fe6W4 | ≤0.02 | ≤1.0 | 4.0-7.0 | ≤0.08 | ≤0.5 | ≥50.0 | 14.5-16.5 | 15.0-17.0 | 3.0-4.5 |
| Grade | % | Ni | Cr | Mo | Fe | W | Co | C | Mn | Si | V | P | S |
| C-276 | Min | Bal. | 14.5 | 15 | 4 | 3 | |||||||
| Max | 16.5 | 17 | 7 | 4.5 | 2.5 | 0.01 | 1 | 0.08 | 0.35 | 0.04 | 0.03 |
| Process | Diameter | Voltage | Amperage | Gas |
| TIG | .045" (1.2mm) | 13-16 | 80-110 | 100% Argon |
| 1/16" (1.6mm) | 14-18 | 90-130 | 100% Argon | |
| 3/32" (2.4mm) | 15-20 | 120-175 | 100% Argon | |
| 1/8" (3.2mm) | 15-20 | 150-220 | 100% Argon | |
| MIG | .045" (1.2mm) | 28-32 | 180-220 | 75% Argon + 25% Helium |
| 1/16" (1.6mm) | 29-33 | 200-250 | 75% Argon + 25% Helium | |
| SAW | 3/32" (2.4mm) | 28-30 | 275-350 | Suitable Flux may be used |
| 1/8" (3.2mm) | 29-32 | 350-450 | Suitable Flux may be used | |
| 5/32" (4.0mm) | 30-33 | 400-550 | Suitable Flux may be used |
Hastelloy | Density g/cm3 | Melting point ºC | Elongation A5 % | Tensile Strength Rm N/mm2 | Yield Strength RP0.2N/mm2 |
C-276 | 8.9 | 1325-1370ºC | 62 | 758 | 363 |
C-22 | 8.9 | 1325-1370 ºC | 40 | 690 | 283 |
C-2000 | 8.5 | 1399ºC 2550°F | 45 | 690 | 283 |
B-2 | 9.2 | 1330-1380ºC | 40 | 745 | 325 |
B-3 | 9.22 | 1370-1418ºC | 40 | 760 | 350 |
G-30 | 8.22 | 1399ºC 2550°F | 62 | 524 | 200 |
X | 8.3 | 1260-1355ºC | 30 | 690 | / |
C-4 | 8.64 | 399°C 2550°F | 40 | 690 | 280 |
G-35 | 8.22 | 1370-1400ºC | / | / | / |
C | 8.94 | 1330-1380 ºC | 40 | 690 | 310 |